Main applications: Used for repairing molten metal. It is made of epoxy resin, curing agent, hardening agent, reactive thinner and various high quality materials. It is used for fast bonding of metal, glass, ceramics, plastic, wood, etc. Used for bubbles, pores or cracks filled in iron and steel foundries, foundry defects, high cure
Hardness, can be used at 100-150 C.
Aggregate performance: White B-gray slurry fitted to the high strength body, high temperature resistance, corrosion resistance, impact resistance, durability, simple operation
Volume ratio: a: B = 1: 1
Curing properties: Hardness: 80 (Shore-D) Shear strength: 18 (25 C)
Complete curing time: 12 hours (25 C)
The bonding process: 1 First, determine the necessary maintenance in clean and spotless conditions. 2. Use files, sandpaper and other tools to process flat surfaces. 3 Apply the full tint of compositions A and B with a volume ratio of 1: 1 to the object to be repaired evenly.
Four hours after finishing all types of processing and 24 hours after gluing.
It must be mixed according to the proportion of components A and B before use, so as not to use any mixture of colors. This is to use, to run out of time. The mixed use time of the adhesive is about 1 hour.
It is stored in the temperature range of 15-28 ° C for up to 24 months. 24 hours after the highest strength, shear strength> 20 MPa (200 kg / M2)